Polycarbonate solid sheets

Polycarbonate Solid Sheets

Brief introduction

  1. Thickness: 0.8mm to 17mm
  2. 100% virgin Bayer/Lexan material
  3. UV protection(One side or two sides)
  4. 10-year warranty
  5. Certificate :ISO9001:2008, ROHS , SGS
  6. High quality & competitive price
  7. Color: clear, green, blue , light blue , brown , opal , red , yellow .
  8. Delivery time :7-10days for 1*40FCL .
  9. Payment : T/T , LC , CASH . 

Standard size 

Normal Width:1200-2100mm

Normal Length: 5800mm, 6000mm , 11800mm

For large order , color and size can be customer made. 

Product Features

General Polycarbonate Solid Sheet has the transparency,but the weight is less than half of the glass ,and has the high impact strength .Gensin  Polycarbonate Solid Sheet can be cold bend ,processed and hot molding .It is widely used in construction and decorations. 

  1. light weight
  2. very high impact strength
  3. Good light transmission
  4. good weather resistance and UV protection
  5. high heat insulation
  6. Simply processed and installed
  7. UV protection layer: 50um
  8. soften temperature : 148℃
  9. continuous use temperature :-40 ~120℃’
  10. certificate by ISO9001:2000,ROHS , SGS

Application

  • lighting
  • indoor window and doors
  • riot windows and doors,shop show window
  • museum show box
  • observe window
  • awning ,carpport
  • indoor partion
  • advertising panel
  • soundbarrier

NORMAL SIZE 

(mm)

Thickness

Standard Width Standard Length Density Color
0.8-17 1200-2100 6000mm

no length limit for sheets thinner than 4mm

1.2 clear

Technical Data

Property Method* Conditions Units Value
Density D-792 g/cm3 1,2
Heat deflection temperature (H.D.T) D-648  Load: 1.82 MPa °C 135
Service Temperature Range (Short term) °C -50 to +120
Service Temperature Range (Long term) °C -50 to +100
Coefficient of linear thermal expansion D-696 mm/cm°C 0.065
Rockwell hardness D-785 R Scale 120
Light transmission D-1003 Clear sheet % 89%
Haze D-1003 Clear sheet % <0.5
Yellowness index D-1003 Clear sheet YI <1.2
Thermal conductivity C-177 W/m K 0.21
Tensile strength at yield D-638 10 mm/min MPa 62
Tensile strength at break D-638 1 mm/min MPa 65
Elongation at yield D-638 10 mm/min % 6
Elongation at break D-638 10 mm/min % >70
Tensile modulus of elasticity D-638 1 mm/min MPa 2,300
Flexural strength mechanical D-790 1 mm/min MPa 93
Flexural modulus D-790 1.3 mm/min MPa 1,890
Impact falling weight (ISO 6603/1 E50) 0.8 mm sheet J 50